Particles for electrophoretic media

ABSTRACT

Compositions of encapsulated triboelectrically charged particles and methods for making them using a spinning disc process are disclosed. The methods can be used to make charged pigment particles embedded in a neutral polymer matrix. The polymer matrix keeps oppositely charged pigment particle from agglomerating. The particles can be used for electrophoretic displays.

This application is a continuation of, and claims priority to, andincorporates by reference U.S. patent application Ser. No. 11/093,857,filed Mar. 30, 2005.

BACKGROUND

1. Technical Field

This disclosure relates to charged particles, such as those used inelectronic paper-like displays, as well as methods for making suchparticles.

2. Description of the Related Prior Art

Paper-like displays based on the electrophoretic migration ofelectrophoretic particles are being developed for use in commercialdisplays, document editing, and document retrieval. Examples of suchdisplays are described in, for example, U.S. Pat. No. 6,517,618 toFoucher et al, U.S. Pat. No. 6,559,820 to Mikkelso Jr. et al, and U.S.Pat. No. 6,411,316 to Shigehiro et al., U.S. Pat. No. 5,961,804 toJacobsen et al., U.S. Pat. No. 6,017,584 to Albet et al., and U.S. Pat.No. 6,067,185 to Albert et. al each of which is incorporated herein byreference in their entirety. In some examples, the electrophoreticparticles may be provided in suspension and sandwiched between one ormore transparent electrodes of the device.

Some such systems are one-particle systems, where a single type ofparticle (usually white) is dispersed in a dark dyed fluid. In aone-particle device, when the particles migrate to the top electrode,the device appears white. When the particles migrate to the bottomelectrode, the white particles are hidden by the dyed fluid, and thedevice appears dark. Another example of a one-particle system involvesbichromal rotating elements where each particle is bichromal, and theparticles selectively rotate in response to an applied electric field toproduce a two-color image. Other such systems are two-particle systems,where the display uses at least two types of particle groups. Theparticle groups have different color and charge characteristics withrespect to each other and move differently when the electric field isapplied. Examples of two-particle displays are disclosed in U.S. Pat.No. 6,657,611 to Machida et al. U.S. Pat. No. 6,525,866 to Lin et al,and U.S. Pat. No. 6,529,313 to Lin et d a, each of which is incorporatedherein by reference in its entirety.

One challenge in the development of two-particle electrophoreticdisplays is the particle design or structure. Each type of particle hasto carry opposite charge so that the particles move in oppositedirections in the electric field created by the electrodes. Theinteraction between these two oppositely charged particles should beminimal to prevent their agglomeration. In addition, the particles mustpossess the requisite chemical and thermal stability to permit their usein the display.

Current methodologies to make two particle electrophoretic displaysystems have focused on the use of different surface polymer coatings onthe pigment particles to stabilize dispersions of the particles in thedisplay. Examples of such coatings are disclosed in U.S. PatentPublication No. 2004/0217929, to Albert et al., and World PatentApplication Publication No. WO02/093246, to Honeyman et al., which areincorporated herein by reference in their entirety. Coated pigmentparticles are difficult to manufacture with consistent performance andat low cost. These kinds of coated particles can suffer fromunpredictable dispersion interaction and poor particle charging, whichlimits device reliability.

Electrophoretic particles that have a polymer coating on the particlesmay be suspended in liquid media. Because of their small size, forexample, about one to about two micron-sized particles, agglomeration isa problem. To prevent particle agglomeration, various combinations ofsurface coating procedures and dispersants are used. However, theincorrect formulation of stabilizers and additives can have an adverseeffect on image bistability, and the image may not persist. The optimumlevel of dispersant draws a fine line between dispersibility and imagepersistence. Furthermore, the stabilizer and dispersant additives arephysioadsorbed onto the electrophoretic particles. Over time andcontinuous particle migration cycles, these additives can desorb fromthe particles and into the surrounding fluid. This can lead to highconductivity of the fluid, dispersion instability (agglomeration), andloss of electrophoretic mobility. For a two-particle system, thecharging mechanism of the particles is more complicated than for aone-particle system. The two types of oppositely charged particles mayinteract with one another and agglomerate. This complicates theformulation of the system.

Another two-particle system is based on dry toners. In this case, tonerparticles typically of an about ten to about twenty micron size arefilled in a micropatterned array and sandwiched between two electrodes.Only an air gap separates the two electrodes. The challenge is theuniform filling of large area grid patterns to accommodate the toner andthe charging of toner by vigorous mechanical tumbling. In the dry tonersystem, high voltages of nearly 400 volts are used to migrate the tonerback and forth across the air gap.

There is a need for electrophoretic particles and compositionscontaining them that form stable dispersions and can be used inelectrophoretic media such as displays. It would be desirable to provideelectrophoretic particles for use in such media at low operatingvoltages further, there is a need to make electrophoretic particles witheasily controlled electrophoretic properties in commercially usefulquantities and in a cost effective manner.

SUMMARY

One embodiment of a composition that may be used in electrophoreticdisplay devices includes triboelectrically charged pigment particlesdispersed in a polymeric matrix. One embodiment of an electrophoreticcomposition may include one or more triboelectrically charged pigmentparticles of like polarity dispersed in a melted polymer matrix. Anotherembodiment of an electrophoretic composition may include one or moretriboelectrically charged pigment particles of like polarity dispersedin the polymeric matrix. The particles may include one or moretriboelectrically charged pigment particles dispersed in the polymermatrix of each particle. The polymeric particles may be spheroidallyshaped, ellipsoidal, substantially spherical and/or spherical althoughother shapes are also possible. She particles of triboelectricallycharged pigment dispersed in the polymer matrix may have anelectrophoretic mobility and density suitable for use in anelectrochromic display. The particles may be prepared to have a mass andsize with a density similar to the dielectric fluid that may be used inthe display; the particles may be near neutrally buoyant and may besuspended without settling in the dielectric fluid used in theelectrochromic display. The electrophoretic particles of the compositionmay be switchable at about ±100 volts to about ±300 volts in anelectrophoretic display, and they may have an electrophoretic mobilityof from about 10⁻⁴ to about 10⁻⁶ cm² sec⁻¹V⁻¹. The particles oftriboelectrically charged pigment dispersed in the polymer matrix may besuspended in a dielectric fluid in which they are nearly neutrallybuoyant. The particles of triboelectrically charged pigment dispersed inthe polymer matrix may be suspended in a dielectric fluid in which theyare nearly neutrally buoyant and further encapsulated by a secondpolymer to form a capsule.

The polymer may have a melt viscosity that permits triboelectriccharging of the pigment particles in the melt as they move across asubstrate. In one embodiment the viscosity of the polymer matrix meltmay be less than about 50 centipoise. In another embodiment theviscosity of the polymer melt may be from about 5 to about 50centipoise. In one embodiment the polymer melt can include an additivethat improves the tribocharging characteristics of the pigment. Inanother embodiment the additive may be, for example, an acetate ester ofa polyethylene-polyethylene oxide copolymer such as X5175 from BakerPetrolite. The additive need not be charge control additives, butimprove the charging characteristics of the pigment. The dropletsreleased from the edge of the moving substrate or spinning disk withcharged pigment particles dispersed in the melted polymeric matrix mayform particles that are spheroidally shaped ellipsoidal, substantiallyspherical, spherical, or a combination of these shapes. Other particleshapes are also possible. The droplets that form electrophoreticparticles and include the charged pigment particles dispersed in themelted polymeric matrix may have a largest dimension of about 250microns or less; for substantially spherical particles this can be adiameter of 250 microns or less. In one embodiment the electrophoreticparticles may have a largest size of from about 0.1 microns to about 250microns. In another embodiment the electrophoretic particles may have alargest size of about 1 to about 10 microns. In one embodiment, thedroplets of charged pigment particles dispersed in the melted polymericmatrix form substantially spherical balls. As an example, thesesubstantially spherical electrophoretic balls when incorporated into anelectrophoretic display device as a suspension may provide a switchingtime in a cell with about 300 micrometer average spacing between theelectrodes of less than about 200 microseconds when the spherical ballsare dispersed in an about 1 centistoke dielectric fluid and a squarewave of about −300 to about +300 volts is applied to the cellelectrodes.

One embodiment of an electrophoretic display can include a cell havingtwo opposed conductive plates separated from each other by an insulatorto form a sealed, such as a fluidly sealed, gas sealed, or airtightsealed, cavity between the plates. Each plate has one or moreelectrodes, where the electrodes can be independently addressable, andwhere at least one of the plates and the one or more electrodes are atleast substantially transparent. The cell cavity may include asuspension of an inert dielectric fluid mixed or combined with one ormore triboelectrically charged encapsulated pigment particles. Thedielectric fluid may include a dye and a single type of electrophoreticparticle (one-particle system). The dielectric fluid may include a firstcolor or achromatic color of electrophoretic particle that is positivelycharged and a second color or achromatic color of electrophoreticparticle that is negatively charged. The individual electrophoreticparticles may be nearly neutrally buoyant in the dielectric fluid, freeof a charge control agent, and include charged pigment particlesdispersed in a polymeric matrix or a polymeric matrix charged bytriboelectric charging. In one embodiment, the pigment particlesdispersed in the polymer matrix are triboelectrically charged.

In one embodiment, the device with the triboelectrically charged pigmentparticles in the polymeric matrix may have a contrast ratio that mayrange from about 5:1 to about 50:1, and the switching time can rangefrom about 50 milliseconds to about 500 milliseconds. In anotherembodiment of the device, the electrophoretic particles of first andsecond color or achromatic color are suspended in a second dielectricfluid and encapsulated by a polymer shell to form one or more capsules,the capsules positioned between the cell plates of the device.

Advantageously the methods and particles prepared by the methods maysimplify the display manufacturing process and reduce or eliminate acharge control agent in the composition or manufacturing process. Thesecoated triboelectric particles may be used in electrophoretic baseddigital document media for a high resolution electronic paper display.

In an embodiment, the particles made by the present method may be nearly100% spherical that provides high quality packing and good opticalperformance. In addition, the pigmented particles may be embedded insidea hard, chemically inert and low surface energy polywax matrix, whichmay minimize particle agglomeration. In some embodiments, the presentprocess can produces particles with size from about 250 microns down toabout 10 microns through adjustments the spinning rate so that nochemical change in formulation is required.

In some embodiments, the triboelectric particles may be used forelectrophoretic based digital display media and for electronic paperdisplay with active matrix drivers.

These and other features, aspects, and advantages of the presentinvention will become better understood with regard to the followingdescription, appended claims, and accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates a schematic setup of an apparatus that may be used tomake polymer coated charged pigment particles.

FIG. 2 presents graphs of dynamic reflectivity measurements.

FIG. 3 illustrates results of dynamic current measurements.

FIG. 4 shows an illustration and optical micrographs of two particledevices in the white (A) and black (B) state.

FIG. 5 is a schematic diagram of an exemplary two-particle displaydevice.

DETAILED DESCRIPTION

As used herein, electrophoresis means the movement of charged particlessuspended in a suspending fluid under the influence of an appliedelectric field. If the electric field is applied between electrodes in acell, the particles may migrate, depending on their polarity, to eitherthe cathode or the anode while the suspending fluid may remainsubstantially stationary. When a coincident voltage is applied toselected electrodes, the particles in the suspending fluid may migrateunder the influence of the electric field to the electrode having apolarity opposite from their own. Since the selection of electrodes maygenerally relate to an image or pattern, the particles may form an imageor pattern.

As used herein, the terms “triboelectrically charged” and “tribocharged”refer to an object that carries an electrical charge that was producedby friction.

One embodiment of an electrophoretic particle composition may includeone or more triboelectrically charged pigment particles dispersed in apolymer matrix. The one or more triboelectrically charged pigmentparticles may be dispersed in the polymer matrix without using solvents.The pigment particles may be triboelectrically charged by movement orflow in a heated thermoplastic material, such as a melted polymer, thattravels across a heated surface such as a spinning surface during theelectrophoretic particle manufacturing process.

To make the electrophoretic particles, the polymer matrix with thepigment particles may be subject to mixing and friction through methodsincluding but not limited to spreading the heated thermoplasticpolymeric material and pigment particles across a heated substrate;heating the matrix and pigment particles and spinning them on a spinningdisk; and/or releasing them in a liquid state as a droplet from aspinning disk. The spreadable or liquid matrix with dispersed chargedparticles may form solid electrophoretic particles by cooling thethermoplastic material below its glass transition temperature to set thecharged pigment particles in the thermoplastic material. In anembodiment, the electrophoretic particles may be substantially sphericalparticles that may be nearly neutrally buoyant in a dielectric fluidwhen used in an electrophoretic display.

The thermoplastic polymer that disperses the charged pigment particlesmay be a material that has a low melt viscosity and that permits thetriboelectric charging of the pigment particles as the mixture ofpolymer melt and pigment particles moves across a heated substrate andbecome charged. The thermoplastic polymer may also becometriboelectrically charged. In one embodiment, the polymer that thecharged pigment particles are dispersed in may be one that has a lowmelt viscosity and that permits the triboelectric charging of thepigment particles as the mixture of polymer melt and pigment particlesmoves across a spinning or rotating disk. The amount of the pigmentparticles in the microcrystalline wax or other base polymer may bechosen to provide the electrophoretic particle with a usefulelectrophoretic mobility and a density for its intended use. The polymermatrix need not contain a charge control agent to charge the particles,and the pigments do not require a coating or charge control agent. Inaddition, the electrophoretic particles can be prepared without the useof solvents. In one version, one or more dyes may be used to color thewax or thermoplastic to give colored triboelectrically chargedelectrophoretic particles.

the base polymer that forms the matrix in which the triboelectricallycharged particles are dispersed can be a thermoplastic, a syntheticmicrocrystalline wax, a crystalline polyethylene wax, or other wax-likematerials that may have a melting point in the range of about 50° C. toabout 200° C. and a sharp melting/crystallization temperature of lessthan about 5° C. Other examples of base polymers include: waxes such ascarnauba wax, candelia wax, castor wax, or the like.

The term “owax” is utilized herein to refer to a low-melting organicmixture of compound of high molecular weight, solid at room temperature,and generally similar in composition to fats and oils except that itcontains no glycerides. Some are hydrocarbons, others are esters offatty acids and alcohols. They are classed among the lipids. Waxes arethermoplastic, but because they are not high polymers, they are notconsidered in the family of plastics. Common properties, are waterrepellency, smooth texture, low toxicity, freedom from objectionableodor and color. They are combustible and have good dielectricproperties; soluble in most organic solvents, insoluble in water. Themajor types are as follows: Natural: (1) Animal (beeswax, lanolin,shellac wax, Chinese insect wax); (2) Vegetable (carnauba, candelilla,bayberry, sugar cane); (3) Mineral: Fossil or earth waxes (ozocerite,ceresin, montan); Petroleum waxes (paraffin, micro-crystalline) (slackor scale wax). Synthetic: (1) Ethylenic polymers and polyol ether-esters(“Carboxwax,” sorbitol); (2) Chlorinated naphthalenes (“Halowax)”, (3)Hydrocarbon type, i.e., Fischer-Tropsch synthesis.

Examples of such commercially available materials and their sourcesinclude polyethylene and polypropylene waxes and their modifiedderivatives. One example of a polyethylene wax is Polywax 1000,manufactured by the Baker-Petrolite Corporation. This material is anearly crystalline polyethylene wax with a narrow molecular weightdistribution, and, consequently, a narrow melt distribution. Thismaterial retains a low melt viscosity until just above the meltingtemperature, a desirable property for the spherodization of theparticles. Other examples include lower molecular weight Polywaxmaterials, such as Polywax 400, Polywax 500, Polywax 600, Polywax 655,Polywax 725, Polywax 850, as well as higher molecular weight Polywaxmaterials such as Polywax 2000, and Polywax 3000. Other examples ofcommercially available polyethylene waxes include members of the Licowaxproduct line, available from Clariant. Examples of such materialsinclude: Licowax PA520 S, Licowax PE130, and Licowax PE520, as well asmicronized polyethylene waxes such as Ceridust 230, Ceridust 3615,Ceridust 3620, and Ceridust 6071.

Examples of commercially available montan waxes include Licolub CaW 3,Licowax E, Licowax OP, all available from Clariant.

A commercially available synthetic form of carnauba wax is Petronauba C,available from Baker-Petrolite Corporation.

Examples of polypropylene waxes include Licomont AR504, Licowax PP230,Ceridust 6071, Ceridust 6072, Ceridust 6721 (Clariant).

Examples of modified polyethylene waxes include linear alcohol waxessuch as: Unilin alcohols including Unilin 350, Unilin 425, Unilin 550and Unilin 700 (Baker-Petrolite Corporation); linear carboxylic acidsuch as Unicid carboxylic acid polymers including Unicid 350, Unicid425, Unicid 550, and Unicid 700 (Baker-Petrolite Corporation), oxidizedpolymer materials such as Cardis 314, Cardis 36, Cardis 320(Baker-Petrolite Corporation) and oxidized polyethylene waxes such asPetrolite C-8500, Petrolite C-7500, Petrolite F-2020, Petrolite C-9500,Petrolite E-040 (Baker-Petrolite Corporation).

Furthermore, in addition to waxes, different polymer materials,including other low polymers, can also be utilized herein so long as thedesired properties and characteristics are produced thereby. Examples ofsuch additional polymers include, but are not limited to, maleicanhydride-ethylene copolymers, maleic anhydride polypropylenecopolymers, nylons, polyesters, polystyrene, poly(chloromethylstyrene),and acrylates such as polymethylmethacrylate.

Commercially available examples of maleic anhydride-ethylene copolymersinclude Ceramer polymers such as Ceramer 1608, Ceramer 1251, Ceramer 67,and Ceramer 5005

(Baker-Petrolite Corporation)

Commercially available examples of maleic functional polypropylenepolymers include X-10036 and X-10016 (Baker-Petrolite Corporation)

Commercially available examples of propylene-ethylene copolymers includePetrolite copolymers such as Petrolite EP-700, Petrolite EP-1104,Petrolite EP-1100, Petrolite EP-1200 (Baker-Petrolite Corporation)

In an embodiment, the base polymer has a low melt viscosity, for examplein the range of about 10 to about 100 centipoise when used to dispersethe charged pigments. In another embodiment, the base polymer has a lowmelt viscosity, for example in the range of about 30 to about 50centipoise when used to disperse the charged pigments. In one embodimentthe thermoplastic may have a viscosity below about 50 centipoise at atemperature of below about 150° C. An example of a material that can beused as a base polymer is a polyethylene was, such as Polywax 1000 fromBaker Petrolite. These properties, a sharp melt transition about 5° C.or less and low melt viscosity, ease the flow of melted wax on thespinning disc and aid in spherical droplet formation and subsequentsphere formation. The size of particles formed by the droplets ofpolymer and charged pigment depends upon the speed of the fluid flowingacross the heated substrate. The particle size may depend inversely onthe rotating speed of the disc and may depend on the melt viscosity ofthe pigmented wax. For example, spinning a disk with a diameter of fromabout a 4 centimeter to about an 8 centimeter at about 5000 to about6000 rotations per minute of can be used to form micron sized particles.Other rotational speeds are also possible for making the sphericalparticles. In one embodiment the particles are about 1 to about 2microns in size, and in another embodiment the particles are about 3 toabout 5 microns in size. The melt viscosity of pigmented wax can bedecreased by using low molecular weight polyethylene, for examplePolywax 850 or Polywax 725, although other materials to modify the meltviscosity with different molecular weights or molecular weightdistributions may also be used.

The particles and material fabrication process can be extended to otherhigher temperature polymer bases such as PW2000 from Baker Petrolite.These higher temperature melting thermoplastic polymers can be used forhigh temperature electrophoretic display applications. The heated movingsubstrate, for example a spinning disk with a shroud heater, can bebrought to a temperature at which the viscosity of the melt is in therange of about 30 to about 50 centipoise. These higher temperaturematerials may eliminate the special cold lamination and post heatingprocess that are often used for two-particle systems to make them stableat high temperatures. In one embodiment the particles are stable up toabout 90° C. and in other embodiments the particle may be stable up toabout 100° C. or more.

Suitable pigments for use in the electrophoretic particle compositionsare those that can be triboelectrically charged. Suitable pigments mayinclude for example TiO₂, ZrO₂, ZnO, Al₂O₃ BaSO₄, CaCO₃, organicpigments, organometallics, other pigments and combinations of these. Inone embodiment, pigments that are chemically and physically compatiblewith the encapsulating polymer or dielectric fluid and aretriboelectrically charged in a polymer matrix. Examples of pigmentsinclude but are not limited to the black pigment Ferro 6331 from FerroInc., which can be positively tribocharged, or a white titania pigmentsuch as titania R104 from E.I. DuPont deNemours & Co. which can betribocharged negatively. Other suitable colorants may include blackcolorants like REGAL 330®; magnetites, such as Mobay magnetites MO8029™,MO8060™; Columbian magnetites; MAPICO BLACKS™ and surface treatedmagnetites; Pfizer magnetites CB4799™, CB5300™, CB5600™, MCX6369™; Bayermagnetites, BAYFERROX 8600™, 8610™; Northern Pigments magnetites,NP-604™. NP-608™; Magnox magnetites TMB-100™, or TMB-104™; and the like,suitable colored pigments or colorants may include, but are not limitedto, cyan, magenta, yellow, red, green, brown, blue colorants or mixturesthereof, other examples of pigments include phthalocyanine HELIOGEN BLUEL6900™, L70201™, D6840™, D7080™, D7020™, K6910™, and K7020™, availablefrom BASF, PYLAM OIL BLUE™, PYLAM OIL YELLOW™, PIGMENT BLUE 1™ availablefrom Paul Uhlich & Company, Inc., PIGMENT VIOLET 1™, PIGMENT RED 48™LEMON CHROME YELLOW DCC 1026™, E.D. TOLUIDINE RED™ and BON RED C™available from Dominion Color Corporation, Ltd., Toronto, Ontario,NOVAPERM YELLOW FGL™, HOSTAPERM PINK E™ from Hoechst, and CINQUASIAMAGENTA™ available from E.I. DuPont de Nemours & Company, and the like;colorants that may be selected are black, cyan, magenta, or yellow, andmixtures thereof, examples of magentas that may be used are2,9-dimethyl-substituted quinacridone and anthraquinone dye identifiedin the Color Index as CI-60710, CI Dispersed Red 15, diazo dyeidentified in the Color Index as CI-26050, CI Solvent Red 19, and thelike; examples of cyans that may be used include copper tetra(octadecylsulfonamido) phthalocyanine, x-copper phthalocyanine pigment listed inthe Color Index as CT 74160, CI Pigment Blue, and Anthrathrene Blue,identified in the Color Index as CI 69810, Special Blue X-2137, and thelike; while illustrative examples of yellows that may be used arediarylide yellow 3,3-dichlorobenzidene acetoacetanilides, a monoazopigment identified in the Color Index as CI 12700, CT Solvent Yellow 16,a nitrophenyl amine sulfonamide identified in the Color Index as ForonYellow SE/GLN, CT Dispersed Yellow 33 2,5-dimethoxy-4-sulfonanilidephenylazo-4′-chloro-2,5-dimethoxy acetoacetanilide, and Permanent YellowFGL. Colored magnetites, such as mixtures of MAPICO BLACK™, and cyancomponents may also be selected as colorants; other known colorants thatmay be selected, such as Levanyl Black A-SF (Miles, Bayer) and SunsperseCarbon Black LHD 9303 (Sun Chemicals), Paliogen Black L9984 9BASF),Pigment Black K801 (BASF) and carbon blacks such as REGAL 330, REGAL 660(Cabot), Carbon Black 5250 and 5750 (Columbian Chemicals), and coloreddyes such as Paliogen Violet 5100 and 5890 (BASE), Normandy MagentaRD-2400 (Paul Uhlrich), Permanent Violet VT2645 (Paul Uhlrich), HeliogenGreen L8730 (BASE), Argyle Green XP-111-S (Paul Uhlrich), BrilliantGreen Toner GR 0991 (Paul Uhlrich), Lithol Scarlet D3700 (BASF), Scarletfor Thermoplast NSD Red (Aldrich), Neopen Blue FF4012 (BASF) Sudan BlueOS (BASF), PV Fast Blue B2G01 (American Hoechst). Sunsperse Blue BLIP6000 (Sun Chemicals), Irgalite Blue BCA (Ciba-Geigy), Paliogen Blue 6470(BASF), Sudan II (Matheson, Coleman, Bell), Sudan III (Matheson,Coleman, Bell), Sudan IV (Matheson, Coleman, Bell), Sudan Orange C(Aldrich), Sudan Orange 220 (BASF), Paliogen Orange 3040 (BASF), OrthoOrange OR2673 (Paul Uhlich), Paliogen Yellow 152, 1560 (BASF), LitholFast Yellow 0991K (BASF), Paliotol Yellow 1840 (BASF), Neopen Yellow(BASF), Novoperm Yellow FG 1, and FGL (Hoechst), Permanent Yellow YE0305 (Paul Uhlich), Lumogen Yellow D0790 (BASF), Sunsperse Yellow YHD6001 (Sun Chemicals), Suco-Gelb L1250 (BASF), Suco-Yellow D1355 (BASF),Sico Fast Yellow D1165, 11355, and D1351 (BASF), Hostaperm Pink E(American Hoechst), Fanal Pink D4830 (BASF), Cinquasia Magenta (DuPont).Lithol Scarlet D3700 (BASE), Toluidine Red (Aldrich), Scarlet forThermoplast NSD PS PA (Ugine Kuhlmann of Canada), E. D. Toluidine Red(Aldrich), Lithol Rubine Toner (Paul Uhlich), Lithol Scarlet 4440(BASF), Bon Red C (Dominion Color Company), Royal Brilliant Red RD-8192(Paul Uhlich), Oracet Pink PF (Ciba-Geigy), Paliogen Red 3871K (BASF),Paliogen Red 3340 (BASE), and Lithol Fast Scarlet L4300 (BASF). Thetriboelectric series can be used as a guide for selecting materials likethe pigment. The average size of the chargeable pigment particles may bein the range of from about 0.05 microns to about 10 microns, althoughother pigment sizes are also possible. By choice of pigment material,the pigment particles can be made with a desired magnitude of charge andpolarity.

The pigment particles can have any color or achromatic color useful in adisplay device. Black, white and gray are not true colors (or hues),they are considered to be neutral, achromatic colors. Pigments that arecomplementary to each other or to a dye in a dielectric fluid used in adisplay device can be used to make electrophoretic particles bytriboelectric charging.

Additives, for example X5175 which may be obtained from Baker PetroliteCorp and which is an acetate ester of a copolymer of polyethylene andpolyethylene oxide with the generic formulaCH₃CH₂—(CH₂CH₂)_(y)(OCH₂CH₂), —OCOCH₃, where y is approximately 13-17and x is approximately 30-50 (also referred to as the acetate ester ofUnithox 480), can be used to improve the tribocharging characteristicsof the pigment particles, such as Ferro 6331 or other black pigments.These and other similar agent or additives are not charge control agentsand may optionally be added to a mixture of pigment and heated wax toimprove the tribocharging characteristics of the mixture.

To form images, electrophoretic displays use a composition that mayinclude a suspension of neutrally buoyant electrophoretic particles, forexample triboelectrically charged pigment particles dispersed within athermoplastic microcrystalline wax or other base polymer, in adielectric fluid. The electrophoretic particles of physically chargedpigment particles embedded in the thermoplastic microcrystalline waxminimize agglomeration or do not agglomerate with each other whensuspended in a dielectric fluid at a concentration used in anelectrophoretic display. The concentration or amount of theseelectrophoretic particles in the dielectric fluid may be chosen toprovide coverage of the cell and contrast for use. In one embodiment theconcentration or amount of these electrophoretic particles in thedielectric fluid may be may be in the range of from about 1% to about20% of the mass of the dielectric fluid. In another embodiment theconcentration or amount of these electrophoretic particles in thedielectric fluid may be in the range of from about 1% to about 30% ofthe mass of the dielectric fluid. In one embodiment the dielectric fluidmay have a kinematic viscosity in the range of about 0.25 centistoke toabout 10 centistoke. In another embodiment the dielectric fluid may havea kinematic viscosity in the range of about 1 centistoke to about 2centistoke. Fluids, such as halogenated organic solvents, saturatedlinear or branched hydrocarbons, silicone oils, and low molecular weighthalogen-containing polymers and combinations of these are some usefuldielectric fluids for electrophoretic particles displays. The dielectricfluid may include a dye for one-particle systems. Oppositely chargedpigment particles coated with a thermoplastic microcrystalline wax donot agglomerate with each other when suspended in a dielectric fluid ata concentration used in an electrophoretic display. The composition canalso include coloring dyes, defoamers and/or other additives used forassembling an electrophoretic display cell.

FIG. 1 illustrates an example of a system with a heated substrate 132that melted thermoplastic material and pigment 120 moves across to formelectrophoretic particles 104. In FIG. 1 the device may include apolymer melt reservoir 116 that dispenses heater polymer with pigmentparticles 120, a spinning disc 132 that triboelectrically charges thepigment and forms droplets 104 of the melted polymer, a shroud heater112 for heating the polymer 134 on the disk, and a nozzle 124 withopening 140 positioned above the spinning disk 132 that can be used todispense a mixture of a melted thermoplastic polymer and pigment 120onto the spinning disk. The spinning disk 132 may be mounted upon arotatable spindle 136. The shroud 144 serves to prevent prematurecooling and solidification of the melted polymer A narrow slit 128between the shroud 144 and disk 132 is where the pigment/polymerdroplets/particles are ejected. The shroud 144 may also serve tominimize any air turbulence that may interfere with particle 104preparation. The liquid and pigment are moved to the periphery of thedisk 132 under the influence of centrifugal force where it separates toform droplets 148 that form particles 104. A disk that is about 4 cm toabout 8 cm in diameter and about 0.0125 to about 0.0250 centimetersthick may be rotated at about 5000 to about 6000 rotations per minutesuccessfully to produces balls about 100 microns or less in diameter.Optionally, the edge of the disk may be contoured to manipulate therelease and size of droplets formed by the heated liquid, for examplethe disk edge may be square, rounded, tapered, or an other shaped edge.

A liquid supply or reservoir 116 may be used to heat and supply thefluid polymeric material to the moving substrate 132. The reservoir 116may be heated, such as to a temperature above the glass transitiontemperature of the wax or thermoplastic, and maintained at thetemperature using a suitable heating system, such as a controller andthermocouple. In one embodiment the pigment and thermoplastic or basepolymer may be added as a mixture to the reservoir by volume or weightpercentage in the range of about 5 wt % to about 40 wt %. In anotherembodiment the pigment and thermoplastic or base polymer may be added asa mixture to the reservoir by volume or weight percentage in the rangeof about 15 wt % to about 30 wt %. Optionally, the mixture may be mixedin the reservoir using a paddle wheel and stir shaft feedthrough tocontact the liquid in the reservoir 116.

The nozzle 124 may also be heated by any suitable heating device, Thenozzle may include a heated or unheated metering valve to automaticallyor manually control the flow rate or amount of liquid with dispersedpigment delivered to the substrate 132. The flow of polymer from thereservoir to the moving substrate may be achieved using a gear pump or apressurized gas in contact with the molten polymer and pigment in thereservoir. The metering valve may be used to control the flow ofmaterial to the substrate. The nozzle tip 140 diameter, tip shape, anddistance from the moving substrate may be modified to produce thedesired fluid profile 134 onto the moving substrate 132.

The pigmented liquids 120 may be delivered to the metering members in aheated, molten state so that they flow freely and do not hardenprematurely, i.e. long enough to prevent the ligaments from freezing. Inone embodiment the pigmented liquids 120 may be delivered to themetering members in a heated, molten state at a temperature of fromabout 100° C. to about 200° C. In another embodiment the pigmentedliquids 120 may be delivered to the metering members in a heated, moltenstate at a temperature of from about 115° C. to about 140° C. A heatingcoil or other heating device may be placed in contact with thestationary liquid delivery assembly. It has been found that with liquidwax, O-rings made of a fluorocarbon rubber such as Viton (trademark ofE.I. DuPont de Nemours & Co.) may be appropriate to withstand therequired temperature and, in fact, are lubricated by the liquid. Ashroud heater 112 may be used to keep the viscosity of the melt in aworking range during the spinning and charging process. A pressure headof about 1 to about 40 pounds per square inch (psi), or from about 5 toabout 10 psi may be used for feeding the liquids through theirrespective paths, to fill the reservoirs and to feed them uniformlythrough metering slots 140 at a thickness of about 0.05 to about 2 mm,or from about 0.1 to about 1 mm onto the surfaces of the movingsubstrate or disk 132. In one version, the pigmented polymer melt may bemetered onto a rotating substrate 132 that triboelectrically chargespigment particles in the polymer melt 120 to form ligaments 148 and,finally, form electrophoretic balls 104.

The liquid material released from the moving substrate should notsolidify prematurely. In an embodiment, the balls should solidify soon,and preferably as soon as possible, after formation. Cooling may beaccelerated by the having the balls pass through a cooling zoneaccomplished by providing a cooled gas or cooled surfaces near the edgeof the substrate where the droplets are formed. The temperature may be agradient to slowly harden the triboelectrically charged particles at anappropriate location (desired shape achieved).

The size the electrophoretic particles may be modified by changing thediameter of the disk, the disk's rotation rate, the molecular weight anddistribution of the polymer, and/or the viscosity of the melted polymerwhen heated. The particle size can be used to modify the response of theparticle to the external field in an electrophoretic device.

The size and density of the charged pigment particles dispersed in thethermoplastic may be used to control the electrophoretic mobility. Theelectrophoretic mobility of the coated charged particles can be on theorder of about 10⁻⁴ to about 10⁻⁶ cm² sec⁻¹V⁻¹. The thickness of thecoating may be modified to control the buoyancy of the particles. In oneembodiment the triboelectric particles may be suspended in a dielectricfluid such that the particles do not float or sink in the fluid.

The substrate material and surface finish, viscosity of the melt, and/orpigment type can be varied to modify the contact area frictional forcesand amount of charge transferred during triboelectric charging. Othervariables such as material work function, back flow of charge and gasbreakdown can affect the amount of charge transferred to the pigment.These variables can be modified by choice of material and processingconditions like rotation rate, to tailor the charge transferred betweenthe substrate and pigment.

Without wishing to be bound by theory, the charging of the particlesprepared in versions of the present method and materials may occur forexample when the pigmented polymer melt contacts and moves across thehigh speed rotating spinning plate. Once the charged pigmented polymermelt leave the disc, the polymer melt may form into a droplet whichfreezes into a sphere or substantially spherical particle and thetriboelectric charge is trapped in the polymer matrix. The sign andmagnitude of the charge of the electrophoretic particles may be modifiedby the polymer melt formulation and omission of additional chargecontrol agents.

Spherical two-particle electrophoretic display systems may have betteroptical bistability than one-particle systems because in thetwo-particle systems the electrophoretic particles can fall from the topelectrode and land on top of other particles without loss of contrast.For example, black particles on white particles or vice versa. Howeverin one-particle systems, once the particles fall from the top electrode,the contrast is lost.

FIG. 4 illustrates a change in the state of a display usingtriboelectrically charged particles. The negatively charged whiteparticles 402 are attracted to the top transparent positive electrode404 while positively charged black particles 406 are attracted to thenegative or ground electrode 408 and the image appears white. When theelectric field is changed the positive black particles 406 are attractedto the negatively charged top electrode 424 while the negatively chargedwhite triboelectrically charged particles are attracted to the bottomrelatively positively charged bottom electrode 428 and the image appearsblack.

The present imaging particles may provide a solvent-less single stepprocess to provide a large quantity of small spherical particles thathave a charged pigment particles embedded in the polymer sphere. Thefinal electrophoretic particle size can be controlled by differentviscosity of pigmented polymer melt and different rotations per minuteof the disc (spinning speed and size of the disk) The particle charge isbuilt inside the spheres through tribocharging and an additional chargecontrol additive is not required.

The optical performance of the two-particle electrophoretic devices maybe monitored by dynamic reflectivity as shown in FIG. 2, and dynamiccurrent as shown in FIG. 3. In FIG. 2, a square wave of about +300 voltsto about −300 volts may be applied across the device (A) and thevariation in reflectivity against time may be simultaneously monitoredin real time by a densitometer (B). In the embodiment shown in FIG. 2,the white reflectivity may be as high as about 28% and the blackreflectivity may be about 6%. The contrast ratio may be about 4.7. Theswitching time may be less than about 200 ms. In FIG. 3, a saw-toothwave form is applied across the device (A). The variation inreflectivity against applied voltage is plotted (B). The maximumreflectivity in this example is attained at about 150 volts. Withoutwishing to be bound by theory, this transition may be further sharpenedby using more uniform size particles. In one embodiment the particlesused to form the device have sizes that are within about 10% or less ofeach other. In another embodiment the particles used to form the devicehave sizes that are within about 5% or less of each other.

One embodiment includes fabricating display devices using capsules. Inthis embodiment two differently colored or different achromatic coloredand charged ink particles are encapsulated by a polymeric binder. Forexample, oppositely charged micron sized electrophoretic particles, forexample from about 1 to about 50 microns, containing tribelectricallycharged black or white pigments in a polymer matrix may be dispersed ina hydrocarbon solvent. For example ink and capsule preparation mayinclude less than about 10% by weight of black and less than about 10%of white electrophoretic particles dispersed in a hydrocarbon baseddielectric fluid like Isopar M®. The prepared ink may be encapsulatedfor example via complex coacervation with gelatin-polyphosphate,gelatin-gum Arabic, or other suitable composition. The microcapsules canbe cross linked to furnish wet deformable capsules. The capsules may bewet sieved to obtain the fraction containing the desired size capsules.

In coacervation, a continuous shell is formed when a water solublepolymer is condensed from an aqueous solution. The shell forms about anucleus of material which becomes the core. Shells of this type based ongelatin and gum arabic are well known. “In situ” polymerization is asecond commonly employed technique for producing microencapsulatedbeads. A shell formed of a gaseous, liquid, water or oil soluble monomeror a low molecular weight polymer is polymerized on the surface of acore material to provide a polymer film which covers the entire surfaceof the core material. Shells based upon urea-formaldehyde are wellknown. A variety of materials including homopolymers, copolymers, graftcopolymers and block copolymers may be used to form the shell.

The term neutrally buoyant refers to the condition where the buoyantforce equals the weight of the particle As noted above, in variousversions of electrophoretic particle compositions, the encapsulatedparticles are generally neutrally buoyant with respect to the liquiddielectric medium. This can be achieved by selectively mixing thepigment particles and the polymer matrix according to a selectedvolumetric ratio so that the density of the particles is close enough tothe density of the dielectric fluid for the particles to be neutrallybuoyant. In one embodiment, the density of the particles may be equalto, or within about five percent of, that of the insulating medium.Settling out of the particles in the display may be greatly reduced oreliminated during periods of non-use.

An electrophoretic device may be fabricated using these capsules, Wetcapsules may be filtered through a filter and mixed with a solutioncontaining a soluble polymer, defoamer, and a plasticizer for thepolymer. A number of different soluble polymer films can be used. A filmmay be formed on an indium tin oxide (ITO) Mylar substrate on theconductive side by spreading the capsules with a blade of appropriategap, in such a way to obtain a monolayer of highly packed capsules. Thefilm may be dried at room temperature. The capsules may be surrounded bya liquid phase which has substantially the same composition as thesuspending liquid within the capsules. The spacing between the platescan also be maintained using spacers. The plates can be sealed to eachother around their peripheries to prevent the liquid external phase fromflowing out of the display. The capsule film may be coated with awaterbase polyurethane glue or other glue by using a blade and thendried. The two substrates can be laminated together to provide the finaldevice which switches between black and white states. The encapsulatedtwo-particle inking may provide the device with flexibility and highcoverage of active switching media.

For electrophoretic displays with triboelectrically chargedelectrophoretic particles using achromatic colored pigments, embodimentscan have a white reflectivity of about 25% or higher and a blackreflectivity of about 10% or lower. In some embodiments the whitereflectivity may be up to about 60% to about 70%. In other embodimentsthe black reflectivity may be from about 1% to about 2% or less. In oneembodiment the contrast ratio may be about 2.5:1 or higher. In anotherembodiment the contrast ratio may be at least about 30:1. In anotherembodiment the contrast ratio may be at least about 50:1. Embodiments ofelectrophoretic displays with triboelectrically charged electrophoreticparticles may have a switching time that is less than about 200milliseconds, or a switching time that can be used for video display. Inone embodiment the switching time may be about 50 milliseconds or higher(switching rate of 20 cycles/second or less).

For addressable electrodes, one or more capsules per pixel can be used.The voltage applied to any of the electrodes in the display can beindependently controlled using an active matrix driver.

As illustrated in FIG. 5 the front electrode 528 is negatively chargedrelative to the rear electrode 512 which is at ground 508. The coatedtriboelectrically charged electrophoretic black particles 540 are heldelectrostatically adjacent the front electrode 528 with outer surface524, while the negatively charged coated triboelectrically charge whiteparticles 548 are held electrostatically against the rear electrode 512with surface 516. Accordingly, an observer viewing the display throughthe front plate sees a black pixel, since the black particles 540 arevisible and hide the white particles.

In the display the front electrode is separated from the rear electrodeby spacers 544. The electrode 532 is connected to a power supply 504 andelectrode 520 may be connected to ground. Transparent protective layers536 and 552 may be applied to the electrodes to chemically protect them.

Various aspects of the present invention will be illustrated withreference to the following non-limiting examples.

EXAMPLE 1

This example illustrates the preparation of triboelectrically chargedparticles in a thermoplastic using a moving substrate to charge thepigment particles.

White pigmented wax-30 grams of TiO₂ (R104 from DuPont) is dispersed in70 g of Polywax 1000 at 130° C. by an IKA T-25 homogenized for 1 hour.Black pigmented wax-20 grams of black pigment (Ferro 6331), 3 grams ofX5175 (Baker Petrolite) is dispersed in 77 g of Polywax 1000 at 130° C.by an IQA T-25 homogenizer for 1 hour.

The pigmented wax is melted and kept in the reservoir at 130-150° C. asillustrated in FIG. 1. The metal disc is spun at 5900-6000 rpm althoughother speeds are possible. The shroud and nozzle temperature are set at150° C. and 130° C. respectively. The particles are collected and sievedthrough a 75 micron screen, then equal amounts of black and whiteparticles are suspended in silicone 200 fluid (1 centistoke, Dow Corningsilicone oils). A drop of suspension is sandwiched between two ITOplates, spacing about 300 microns, and the switching voltage is about±(100-300) volts.

EXAMPLE 2

This example illustrates the fabrication of an electrophoretic displaythat incorporates capsules with one or more coated triboelectricallycharged pigment particles.

One embodiment includes fabricating devices by using encapsulated2-particle ink into a polymeric binder. Micron sized electrophoreticparticles black and white, prepared as described in Example 15 aredispersed in a hydrocarbon solvent like Isopar Mt. For example ink andcapsule preparation includes 5 grams of a black and 5 grams of a whiteink prepared as described is dispersed in 35 g of Isopar M®. Theprepared ink is encapsulated via complex coacervation withgelatin-polyphosphate or gelatin-gum Arabic. The microcapsules are crosslinked with gluteraldehyde to furnish wet deformable capsules. Thecapsules are wet sieved to obtain the desired fraction containingcapsules of 212 to 180 micron size.

A device can be fabricated using the capsules. For example, 6 grams ofwet capsules are filtered through a paper filter and then they are mixedwith a solution containing 0.5 ml of PVA 30%, 3 drops of 1-octanol(defoamer) and 75 milligrams of glycerol (plasticized for PVA). A filmwas formed on an ITO/Mylar substrate (5 mils thick; about 0.0125 cm), onthe conductive side by spreading the capsules with a blade ofappropriate gap, in such a way to obtain a monolayer of highly packedcapsules. The film is dried at room temperature overnight. The capsulesdeform during the dewatering process. The film is coated with NeoRez(waterbase polyurethane glue) by using a blade, then dried for one hourat 60° C. The two substrates are laminated together to provide the finaldevice which switches between black and white states. The encapsulatedtwo-particle ink provides the device with flexibility and high coverageof active switching media.

Although the disclosure has provided considerable detail with referenceto certain preferred embodiments thereof, other versions are possible.Therefore the spirit and scope of the appended claims should not belimited to the description and the preferred versions contain withinthis specification.

1. A composition comprising. one or more triboelectrically chargedpigment particles dispersed and embedded within a polymer matrix,wherein the polymeric matrix includes an additive that improves thetribocharging characteristics of the pigment.
 2. The composition ofclaim 1 wherein the polymer matrix comprises a melt having a viscosityof less than about 50 centipoise.
 3. The composition of claim 1 whereinthe polymer matrix comprises a melt having a viscosity of between about5 to about 50 centipoise.
 4. The composition of claim 1 wherein thepolymer matrix comprises a wax selected from the group consisting of athermoplastic a synthetic microcrystalline wax, a crystallinepolyethylene wax, and other wax-like materials having a melting pointfrom about 50° C. to about 200° C. and a sharp melting orcrystallization temperature of less than about 5° C.
 5. The compositionof claim 1 wherein the additive comprises an oxide.
 6. The compositionof claim 1 wherein the additive comprises an acetate ester of acopolymer of polyethylene and polyethylene oxide.
 7. The composition ofclaim 1 wherein the pigment particles comprise spherically shapedparticles.
 8. The composition of claim 1 wherein the pigment particlescomprise one or more of the following: TiO₂, ZrO₂, ZnO, Al₂O₃, BaSO₄,and CaCO₃.
 9. The composition of claim 1 wherein the pigment particlescomprise one or more of the following: an organic pigment and anorganometallic.
 10. The composition of claim 1 wherein the particles areused in an electrophoretic display device.
 11. The composition of claim1 wherein the particles have an electrophoretic mobility and density foruse in an electrochromic display.
 12. The composition of claim 1 furtherincluding a dielectric fluid.
 13. The composition of claim 1 wherein thecomposition comprises at least two groups of particles having differentelectrophoretic properties.
 14. The composition of claim 13 where theparticles are buoyant and suspended without settling in the fluid.
 15. Acomposition comprising: one or more triboelectrically charged pigmentparticles dispersed and embedded within a polymer matrix, wherein thepolymeric matrix includes an additive that improves the tribochargingcharacteristics of the pigment; and wherein the additive comprises anacetate ester of a copolymer of polyethylene and polyethylene oxide, andthe composition further including a dielectric fluid where the particlesare buoyant and suspended without settling in the fluid.
 16. Thecomposition of claim 15 wherein the pigment particles comprise one ormore of the following: TiO₂ ZrO₂, ZnO, Al₂O₃, BaSO₄, and CaCO₃.
 17. Thecomposition of claim 15 wherein the pigment particles comprise one ormore of the following: an organic pigment and an organometallic.
 18. Acomposition comprising: one or more triboelectrically charged pigmentparticles dispersed and embedded within a polymer matrix, wherein thepolymeric matrix includes an additive that improves the tribochargingcharacteristics of the pigment; and wherein the additive comprises anoxide, and the composition further including a dielectric fluid wherethe particles are buoyant and suspended without settling in the fluid.